Low alloy tool steel, mat. no. 1.2604
-
Price:
Negotiable
- minimum:
- Total supply:
-
Delivery term:
The date of payment from buyers deliver within days
-
seat:
Beijing
-
Validity to:
Long-term effective
-
Last update:
2017-12-16 05:38
-
Browse the number:
120
+
Shanghai Bozhong Metal Group Co. Ltd
- Contactaixin:
bozhong(Ms.)
-
Email:
telephone:
-
Arrea:
Beijing
Address:BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website:
+
Model Number: ZXL037
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionLow alloyed cold working tool steelApplicationsTap drills, broaching tools, milling cutters and other cutting tools. It is usually supplied as silver steelChemical composition (in weight%)C: 0.73
Si: 0.30
Mn: 0.50
Cr: 0.50
W: 0.55
Mo: 0.33
V: 0.23
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Soft annealing
Heat to 680-710℃, cool slowly. This will produce a maximum Brinell hardness of 225
Hardening
Harden froma temperature of 810-840℃, followed by oil quenching. Hardness after quenching is 63HRC
Tempering
Tempering temperature: 180-300℃
Forging
Hot forming temperature: 1050-900℃
Machinability
The machinabillity rating of D3 is roughly 25% that of free machining carbon steel 1018. Due to its abrasion resistant nature, machining in the hardened condition should be limited to finish grinding
Specifications:
Grade: mat. no. 1.2604
Standard: DIN, GB
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
Si: 0.30
Mn: 0.50
Cr: 0.50
W: 0.55
Mo: 0.33
V: 0.23
Physical properties (averagevalues) at ambient temperature
Modulus of elasticity [103xN/mm2]: 210
Density [g/cm3]: 7.80
Soft annealing
Heat to 680-710℃, cool slowly. This will produce a maximum Brinell hardness of 225
Hardening
Harden froma temperature of 810-840℃, followed by oil quenching. Hardness after quenching is 63HRC
Tempering
Tempering temperature: 180-300℃
Forging
Hot forming temperature: 1050-900℃
Machinability
The machinabillity rating of D3 is roughly 25% that of free machining carbon steel 1018. Due to its abrasion resistant nature, machining in the hardened condition should be limited to finish grinding
Specifications:
Grade: mat. no. 1.2604
Standard: DIN, GB
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot rolled
Packing and delivery
Packing: standard export seaworthy package or as customers’requirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
- Dimensions per Unit: 6 × 2 × 0.2 Meters
- Weight per Unit: 20 Kilograms
- Units per Export Carton: 5
- Export Carton Dimensions L/W/H: 6 × 2 × 0.2 Meters
- Export Carton Weight: 5 Tons (US)
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe